000			04425nam a22002657a 4500
003			OSt
005			20180913154445.0
008			170725b xxu||||| |||| 00| 0 eng d
040			_aUnicoc _bspa _cUNICOC
082			_aT.O.Pr.0077
100			_96023 _aKamal Echtay, Harba Youssef
245			_aComportamiento de la unión metal cerámica ante las fuerzas de cizallamiento de cilindros colados vs sinterizados en co-cr. _cHarba Youssef Kamal Echtay
260			_aBogotá (Colombia); _bInstitución Universitaria Colegios de Colombia - UNICOC; _c2017.
500			_aIncluye tabla de contenido y referencias bibliográficas
504			_aAsesor científico: Dra. Mónica Forero; Asesor Metodológico: Diana Parra.
505			_tRESUMEN Introducción: comparar el comportamiento ante fuerzas de cizallamiento en la unión metal-cerámica utilizando cilindros de Co-Cr sinterizadas vs coladas. Materiales y métodos: investigación experimental in vitro, utilizando 36 cilindros de metal base Co-Cr colados y sinterizados de 9mm de longitud por 2.5 mm de diámetro (n = 18 por grupo). La muestra total se subdividió en 4 grupos (n=9) a los cuales se les añadió 2mm de porcelana (cerámica Vita), sometiendo a termociclado a dos de los grupos. Un experto realizó prueba de cizallamiento al total de la muestra con una máquina universal de ensayos (Instron), el cual se encargó de interpretar los resultados obtenidos de micrografías tomadas en los lugares donde se producían las fallas en los cilindros (colados y sinterizados). Resultados: la fuerza media de cizallamiento en los cilindros sinterizados sin termociclado fue de 63,56MPa, y de 51,52MPa; en los cilindros colados esta fuerza para ambos casos, fue cercana a los 40MPa; grupos que presentaron diferencias estadísticas (p=0,0002). Las principales fallas que se presentaron fueron las adhesivas (n=31; 88,57%), seguida de las mixtas (n=5, 11,43%); no se presentaron fallas cohesivas (p=0,465). Conclusiones: los cilindros sinterizados sin y con termociclado presentaron un mejor comportamiento ante la presencia de fuerzas de cizallamiento que los cilindros colados. Además, sin diferencias importantes entre los grupos, se presentan prevalentemente fallas adhesivas
505			_tABSTRACT Overall objective: to compare strengthening forces at the metal-ceramic bond using sintered vs. cast Co-Cr cylinders. Materials and methods: In vitro experimental investigation, using 36 cast and sintered Co-Cr base metal cylinders 9mm long by 2.5 mm diameter (n = 18 per group). The total sample was subdivided into 4 groups (n = 9) to which 2mm of porcelain (Vita ceramics) were added, subjecting two of the groups to thermocycling. An expert performed the shear test with the universal test machine assembly (Instron), which was responsible for interpreting the results obtained from micrographs taken in the places where the failures in the cylinders (cast and sintered) occurred. Results: the mean shear force in the sintered cylinders without thermocycling was 63.56MPa, and 51.52MPa; In the cast cylinders this force for both cases were close to 40MPa; groups that presented statistical differences (p=0.0002). The main faults presented were adhesives (n = 31, 88.57%), followed by mixtures (n = 5, 11.43%); there were no cohesive failures (p=0.465). Conclusions: sintered cylinders without and with thermocycling showed a better performance in the presence of shear forces than the cast cylinders. In addition, with no significant differences between groups, adhesive failures occur predominantly
505			_tPalabras clave: cobalto-cromo, termociclado, fallas adhesivas, fallas cohesivas, aleaciones, sinterizado, colado, tecnología CAD/CAM, fuerza de cizallamiento, falla del material ; -Keywords: cobalt-chromium, thermocycling, adhesive faults, cohesive failure, alloys, sintering, casting, CAD / CAM technology, shearing force, material failure
650		0	_9392 _aOdontología / Prostodoncia - Tesis y disertaciones académicas.
700			_96024 _aCórdoba Duran, Jesús Arcesio
700			_96026 _aRojas Tique, Liliana Alejandra
700			_96025 _aMatiz Gracia, Diego Nicolás
773			_dBogotá, Institución Universitaria Colegios de Colombia - UNICOC, 2017. _tComportamiento de la unión metal cerámica ante las fuerzas de cizallamiento de cilindros colados vs sinterizados en co-cr. _x20171TOPr0077
942			_2ddc _cTESIS
999			_c8399 _d8399